Low Alloy STAW Welding -- Welding Electrode for Low Alloy Steel Structures
| Chemical Composition (%) |
Classification |
| |
C |
Mn |
Si |
Ni |
Cr |
Mo |
Cu |
P |
S |
AWS |
GB |
JIS |
DIN |
| Typical Values |
0.072 |
1.24 |
0.49 |
0.7 |
|
|
|
0.015 |
0.012 |
A5.5 E8015-G |
J557 |
D5316 |
EY5066NiMoBH5 |
| General Values |
≤0.12 |
≥1.0 |
0.30-0.70 |
0.5-1.0 |
|
|
|
≤0.040 |
≤0.035 |
EN |
ISO 2560-A E 50 6 Mn1Ni B 12 H5(Similiar) |
| |
Tensile Strength ( Mpa) δb |
Yield Strength ( Mpa) δs |
Elongation (%) δ5 |
Welding Position |
Test Temp. |
Impact Values,Akv (J) |
| Typical Values |
640 |
476 |
27 |
F.V.OH.H. |
-30℃ |
63 |
| General Values |
≥540 |
≥440 |
≥17 |
-40℃ |
≥27 |
| Chemical Composition (%) |
Classification |
| |
C |
Mn |
Si |
Ni |
Cr |
Mo |
Cu |
P |
S |
AWS |
GB |
JIS |
DIN |
| Typical Values |
0.076 |
1.24 |
0.49 |
0.37 |
1.1 |
0.7 |
0.26 |
0.015 |
0.012 |
A5.5 E7015-G |
J507CrNi |
|
|
| General Values |
≤0.12 |
0.5-0.8 |
0.30-0.70 |
0.2-0.5 |
0.6-1.4 |
0.4--1.0 |
0.2-0.5 |
≤0.035 |
≤0.035 |
EN |
ISO 2560-A E Cr Mo1L B 2 2 H5(Similiar) |
| |
Tensile Strength ( Mpa) δb |
Yield Strength ( Mpa) δs |
Elongation (%) δ5 |
Welding Position |
Test Temp. |
Impact Values,Akv (J) |
| Typical Values |
580 |
450 |
30 |
F.V.OH.H. |
-30℃ |
72 |
| General Values |
≥520 |
≥410 |
≥22 |
-40℃ |
≥27 |
| Chemical Composition (%) |
Classification |
| |
C |
Mn |
Si |
Ni |
Cr |
Mo |
Cu |
P |
S |
AWS |
GB |
JIS |
DIN |
| Typical Values |
0.082 |
1.34 |
0.45 |
1.65 |
1.6 |
1.8 |
0.08 |
0.015 |
0.012 |
A5.5 E9015-G |
J607RH |
D5816 |
DY5554BXXH5 |
| General Values |
≤0.12 |
1.20-1.60 |
0.30-0.60 |
1.4-2.0 |
0.08-0.20 |
0.25-0.50 |
|
≤0.035 |
≤0.035 |
EN |
ISO 2560-A |
E Cr Mo 91 B 42 |
H5 (Similiar) |
| |
Tensile Strength ( Mpa) δb |
Yield Strength ( Mpa) δs |
Elongation (%) δ5 |
Welding Position |
Test Temp. |
Impact Values,Akv (J) |
| Typical Values |
760 |
580 |
21 |
F.V.OH.H. |
20℃ |
90 |
| General Values |
≥620 |
≥530 |
≥15 |
0℃ |
≥27 |
| Chemical Composition (%) |
Classification |
| |
C |
Mn |
Si |
Ni |
Cr |
Mo |
Cu |
P |
S |
AWS |
GB |
JIS |
DIN |
| Typical Values |
0.086 |
1.6 |
0.3 |
1.3 |
0.42 |
0.4 |
|
|
|
A5.5 E11015-G |
J757Ni |
D7016 |
EY6924BXXH15 |
| General Values |
≤0.10 |
≥1.0 |
≤0.60 |
1.0-1.5 |
0.25-0.60 |
0.3-0.5 |
|
≤0.035 |
≤0.035 |
EN 757 |
E 69 5 Mn2 NiMo 91 B 53 H5(Similiar) |
| |
Tensile Strength ( Mpa) δb |
Yield Strength ( Mpa) δs |
Elongation (%) δ5 |
Welding Position |
Test Temp. |
Impact Values,Akv (J) |
| Typical Values |
790 |
760 |
20 |
F.V.OH.H. |
20℃ |
85 |
| General Values |
≥740 |
≥640 |
≥13 |
-20℃ |
≥27 |
Loy Alloy GMAW Welding------MIG/MAG Welding Wire for Low Alloy Structures
| Chemical Composition (%) |
Classification |
| |
C |
Mn |
Si |
Ni |
Cr |
Mo |
Cu |
P |
S |
AWS |
GB |
JIS |
DIN |
| Typical Values |
0.08 |
1.36 |
0.92 |
0.2 |
1.2 |
0.45 |
0.15 |
0.012 |
0.008 |
A5.28 ER80S-G |
ER59-G |
|
|
| General Values |
0.06-0.15 |
1.0-1.60 |
0.80-1.15 |
|
0.80-1.60 |
0.3-0.6 |
≤0.5 |
≤0.030 |
≤0.030 |
EN |
ISO 21592-A GCrMo1Si / ISO 14341-A G3Ni1 |
| |
Tensile Strength ( Mpa) δb |
Yield Strength ( Mpa) δs |
Elongation (%) δ5 |
Shielding Gas |
Test Temp. |
Impact Values,Akv (J) |
| Typical Values |
720 |
508 |
28 |
80% Ar + 20% CO2
recommended |
26℃ |
103 |
| General Values |
≥590 |
≥450 |
≥16 |
20℃ |
≥27 |
Low Alloy SAW Welding------Submerged Arc Welding Wire for Low Alloy Structures
| Chemical Composition (%) |
Classification |
| |
C |
Mn |
Si |
Ni |
Cr |
Mo |
Cu |
P |
S |
AWS |
GB |
JIS |
DIN |
| Typical Values |
0.09 |
1.26 |
0.16 |
0.02 |
|
0.52 |
0.15 |
|
|
A5.23 EA2 |
H08MnMoA |
|
|
| General Values |
0.05-0.17 |
0.95-1.35 |
≤0.20 |
|
|
0.45-0.65 |
≤0.35 |
≤0.025 |
≤0.025 |
EN 756 |
S2 Mo |
| |
Tensile Strength ( Mpa) δb |
Yield Strength ( Mpa) δs |
Elongation (%) δ5 |
Recommended Flux -- SFA/AWS A5.17 |
Test Temp. |
Impact Values,Akv (J) |
| Typical Values |
632 |
536 |
26 |
Refer to specification Guide of
Lincoln/Esab |
-30℃ |
70 |
| General Values |
≥590 |
≥490 |
≥23 |
-30℃ |
≥27 |
| Chemical Composition (%) |
Classification |
| |
C |
Mn |
Si |
Ni |
Cr |
Mo |
Cu |
P |
S |
AWS |
GB |
JIS |
DIN |
| Typical Values |
0.09 |
1.90 |
0.14 |
|
|
0.49 |
0.13 |
|
|
A5.23 EA3 |
H08Mn2MoA |
|
|
| General Values |
0.05-0.17 |
1.65-2.20 |
≤0.20 |
|
|
0.45-0.65 |
≤0.35 |
≤0.025 |
≤0.025 |
EN 756 |
S4 Mo (Similiar) |
| |
Tensile Strength ( Mpa) δb |
Yield Strength ( Mpa) δs |
Elongation (%) δ5 |
Recommended Flux -- SFA/AWS A5.17 |
Test Temp. |
Impact Values,Akv (J) |
| Typical Values |
710 |
620 |
27 |
Refer to specification Guide of
Lincoln/Esab |
-20℃ |
85 |
| General Values |
≥620 |
≥550 |
≥24 |
-40℃ |
≥27 |
Low Alloy TIG Welding------Argon Arc Welding Wire for Low Alloy Structures
| Chemical Composition (%) |
Classification |
| |
C |
Mn |
Si |
Ni |
Cr |
Mo |
Cu |
P |
S |
AWS |
GB |
JIS |
DIN |
| Typical Values |
0.11 |
1.42 |
0.82 |
0.2 |
1.2 |
0.45 |
0.26 |
0.016 |
0.012 |
A5.28 ER80S-G |
ER59-G |
|
|
| General Values |
0.06-0.15 |
1.0-1.60 |
0.80-1.15 |
|
0.80-1.60 |
0.3-0.6 |
≤0.5 |
≤0.030 |
≤0.030 |
EN |
|
| |
Tensile Strength ( Mpa) δb |
Yield Strength ( Mpa) δs |
Elongation (%) δ5 |
Shielding Gas |
Test Temp. |
Impact Values,Akv (J) |
| Typical Values |
680 |
500 |
29 |
Ar |
26℃ |
82 |
| General Values |
≥590 |
≥450 |
≥16 |
20℃ |
≥27 |
Mild Steel FCAW Welding------Flux-Cored Welding Wire for Mild Steel Structures
| Chemical Composition (%) |
Classification |
| |
C |
Mn |
Si |
Ni |
Cr |
Mo |
Cu |
P |
S |
AWS |
GB |
JIS |
DIN |
| Typical Values |
0.07 |
1.16 |
0.36 |
0.94 |
0.06 |
0.48 |
|
|
|
A5.29 E81T1-Ni1 |
YC-YJ602(Q) |
YFW-C603R |
|
| General Values |
≤0.15 |
0.80-1.40 |
≤0.70 |
0.80-1.10 |
≤0.15 |
0.20-0.65 |
|
≤0.030 |
≤0.030 |
EN |
ISO 17632-A T 46 3 1Ni P C 2 H5 (Similiar) |
| |
Tensile Strength ( Mpa) δb |
Yield Strength ( Mpa) δs |
Elongation (%) δ5 |
Shielding Gas |
Test Temp. |
Impact Values,Akv (J) |
| Typical Values |
630 |
550 |
32 |
CO2 |
-40℃ |
76 |
| General Values |
550-690 |
≥470 |
≥27 |
-40℃ |
≥27 |
|
|
|
|
|