Mild Steels  Mild Steel STAW Welding--Welding Electrode for Mild Steel Structures                                                                            Chemical Composition (%)                                                Classification 　    C    Mn    Si Ni Cr Mo Cu P S     AWS   GB   JIS DIN Typical Values    0.09    0.45    0.15 　 　 　 　 　 　 A5.1 E6013 J421 D4313 E4332 R3 General Values ≤0.12 0.30-0.60 ≤0.35 　 　 　 　 ≤0.040 ≤0.035     EN   ISO 2560-A   E 42 0 RR 12 　 Tensile Strength ( Mpa) δb  Yield Strength ( Mpa)  δs Elongation (%) δ5                    Welding Position     Test Temp. Impact Values,Akv (J) Typical Values                       410                    509              33                    F.V.OH.H.VD.          0℃             63 General Values                    ≥420                 ≥330           ≥22          0℃          ≥27                                                                            Chemical Composition (%)                                                Classification 　    C    Mn    Si Ni Cr Mo Cu P S     AWS   GB   JIS DIN Typical Values    0.07    1.36     0.58 　 　 　 　 　 　 A5.1 E7018 J506Fe D5016 E5154B(R)10 General Values ≤0.12 ≤1.60 ≤0.75 　 　 　 　 ≤0.040 ≤0.035     EN   ISO 2560-A E 42 4 B 42 H 5 　 Tensile Strength ( Mpa)    δb  Yield Strength ( Mpa)   δs Elongation (%) δ5                   Welding Position    Test Temp. Impact Values,Akv (J) Typical Values                       516                     615              31                   F.V.OH.H.     -20℃            106 General Values                    ≥490                  ≥400           ≥22     -30℃           ≥27                                                                            Chemical Composition (%)                                                Classification 　    C    Mn    Si Ni Cr Mo Cu P S     AWS   GB   JIS DIN Typical Values    0.07    0.8     0.42 　 　 　 　 　 　 A5.1 E7016  J506 D5016 E51431310 General Values ≤0.15 ≤1.25 ≤0.90 　 　 　 　 ≤0.040 ≤0.035     EN   ISO 2560-A   E42 4 B 42 H 5 　 Tensile Strength ( Mpa)    δb  Yield Strength ( Mpa)   δs Elongation (%) δ5                   Welding Position    Test Temp. Impact Values,Akv (J) Typical Values                       560                    420              28                  F.V.OH.H.     -20℃            80 General Values                    490-660                 ≥375           ≥22     -30℃         ≥27                                                                             Chemical Composition (%)                                                Classification 　    C    Mn    Si Ni Cr Mo Cu P S     AWS   GB   JIS DIN Typical Values    0.13    0.46    0.17 　 　 　 　 　 　 A5.1 E6010 J425 D4313 E4333 R (C) 3 General Values 0.09-0.17 0.40-0.79 0.09-0.32 　 　 　 　 ≤0.040 ≤0.035     EN   ISO 2560-A   E 42 3 C25 　 Tensile Strength ( Mpa)    δb  Yield Strength ( Mpa)   δs Elongation (%) δ5                   Welding Position    Test Temp. Impact Values,Akv (J) Typical Values                       572                    452              32                  F.V.OH.H.VD--All POSITION    -20℃            89 General Values                    ≥430                 ≥330           ≥22    -30℃         ≥27 Mild Steel GMAW Welding--MIG/MAG Welding Wire for Mild Steel Structures                                                                            Chemical Composition (%)                                                Classification 　    C    Mn    Si Ni Cr Mo Cu P S    AWS   GB   JIS DIN Typical Values    0.08    1.5    0.92 　 　 　 0.16 　 　 A5.18 ER70S-6 ER50S-6 YGW12 8559 SG2 General Values 0.06-0.15 1.40-1.85 0.80-1.15 　 　 　 　 ≤0.040 ≤0.035     EN 440 ISO 14341-A   G 46 4 M G3Si1 / G4Si1 　 Tensile Strength ( Mpa)    δb  Yield Strength ( Mpa)   δs Elongation (%) δ5                  Shielding Gas    Test Temp. Impact Values,Akv (J) Typical Values                       569                    457               32                 75%-95% Ar + Rest CO2:                           CO2;    26℃           103 General Values                    ≥500                 ≥420            ≥22    20℃          ≥27                                                                          Chemical Composition (%)                                                Classification 　    C    Mn    Si Ni Cr Mo Cu P S     AWS   GB   JIS DIN Typical Values    0.08    1.18    0.58 　 　 　 0.20 　 　 A5.18 ER70S-3 ER50S-3 　 YGW16 General Values ≤0.15 0.90-1.40 0.45-0.75 　 　 　 ≤0.50 ≤0.025 ≤0.035     EN 440 ISO 14341-A G 42 2 M G2Si 　 Tensile Strength ( Mpa)    δb  Yield Strength ( Mpa)   δs Elongation (%) δ5                      Shielding Gas    Test Temp. Impact Value,Akv(J) Typical Values                       536                    446               27                    75%-95% Ar + Rest CO2                    CO2;           20℃            106 General Values                    ≥490                 ≥400            ≥22    0℃           ≥27 Mild Steel SAW Welding--Submerged Arc Welding Wire for Mild Steel Structures                                                                            Chemical Composition (%)                                                Classification 　    C    Mn    Si Ni Cr Mo Cu P S     AWS   GB   JIS DIN Typical Values    0.08    0.47    0.02 　 　 　 0.20 　 　 A5.17 EL12 H08A 　 S1 General Values ≤0.12 0.30-0.60 ≤0.10 　 　 　 ≤0.50 ≤0.030 ≤0.030     EN 756 S1 　 Tensile Strength ( Mpa)    δb  Yield Strength ( Mpa)   δs Elongation (%) δ5  Recommended Flux -- SFA/AWS A5.17    Test Temp. Impact Values,Akv (J) Typical Values                       508                    379               30  Refer to specification Guide of Lincoln/Esab     0℃           88 General Values                    410-550                 ≥330            ≥22    0℃        ≥27                                                                            Chemical Composition (%)                                                Classification 　    C    Mn    Si Ni Cr Mo Cu P S     AWS   GB   JIS DIN Typical Values    0.07    0.92    0.56 　 　 　 　 　 　 A5.17 EM12 H08MnA 　 S2 General Values ≤0.12 0.80-0.11 ≤0.90 　 　 　 　 ≤0.040 ≤0.035     EN 756 S2 　 Tensile Strength ( Mpa)    δb  Yield Strength ( Mpa)   δs Elongation (%) δ5  Recommended Flux -- SFA/AWS A5.17    Test Temp. Impact Values,Akv (J) Typical Values                       570                    431               29 Refer to specification Guide of Lincoln/Esab     -40℃            89 General Values                    480-650                 ≥360            ≥22    -40℃         ≥27 Mild Steel TIG Welding------Argon Arc Welding Wire for Mild Steel Structures                                                                            Chemical Composition (%)                                                    Classification 　    C    Mn    Si Ni Cr Mo Cu P S     AWS   GB   JIS DIN Typical Values    0.08    1.62    0.90 　 　 　 0.2 　 　 A5.18 ER70S-6 ER50S-6 YGW12 8559 SG2 General Values 0.06-0.15 1.40-1.85 0.80-1.15 　 　 　 　 ≤0.040 ≤0.035     EN 1668 W 42 5 W3Si1 　 Tensile Strength ( Mpa)    δb  Yield Strength ( Mpa)   δs Elongation (%) δ5                   Shielding Gas    Test Temp. Impact Value,Akv (J) Typical Values                      560                    470               29                 Argon;                    Argon + Hydrogen or Helium    -30℃                  82 General Values                   ≥500                 ≥420            ≥22    -30℃               ≥27                                                                         Chemical Composition (%)                                                        Classification 　    C    Mn    Si Ni Cr Mo Cu P S     AWS  GB JIS DIN Typical Values    0.08    1.18    0.58 　 　 　 0.16 　 　 A5.18 ER70S-3 ER50S-3 　 YGW16 General Values ≤0.15 0.90-1.40 0.45-0.75 　 　 　 ≤0.50 ≤0.025 ≤0.035 EN 1668 W 42 5 W2Si 　 Tensile Strength ( Mpa)    δb  Yield Strength ( Mpa)   δs Elongation (%) δ5  Shielding Gas    Test Temp. Impact Value,Akv (J) Typical Values                       536                    422              28 CO2;                                                                     75%-95% Ar + Rest CO2:           20℃            87 General Values                    470-600                 ≥380           ≥22     0℃         ≥27 Mild Steel FCAW Welding------Flux-Cored Welding Wire for Mild Steel Structures                                                                            Chemical Composition (%)                                                Classification 　    C    Mn    Si Ni Cr Mo Cu P S     AWS   GB   JIS DIN Typical Values    0.08    1.22    0.56 　 　 　 　 　 　 A5.20 E71T-1 YC-YJ502(Q) YFW-C50DR 　 General Values ≤0.12 0.50-1.85 0.30-0.90 　 　 　 　 ≤0.030 ≤0.030     EN   ISO 17632-A   T 46 2 P C 2 H10 　 Tensile Strength ( Mpa)    δb  Yield Strength ( Mpa)   δs Elongation (%) δ5                   Shielding Gas    Test Temp. Impact Values,Akv (J) Typical Values                      560                    550              36                  CO2    -20℃           120 General Values                   550-690                 ≥470           ≥26    -20℃          ≥27 Home  |  About Us  |  Product Catalog  |  Welding Application  |  Welding Process  |  Industry News  |  Contact Us  |  Sitemap Rights reserved by "Precision Welding Material Group of Hebei China" Powered by DIYTrade.com